Mechanical performance of polymer-infiltrated zirconia ceramics

Li, Jing ; Zhang, Xue-Hui ; Cui, Ben-Cang ; Lin, Yuan-Hua ; Deng, Xu-Liang ; Li, Ming ; Nan, Ce-Wen

Journal of dentistry, 2017-03, Vol.58, p.60-66 [Periódico revisado por pares]

England: Elsevier Ltd

Texto completo disponível

Citações Citado por

Enviar para

Título:
Mechanical performance of polymer-infiltrated zirconia ceramics
Autor: Li, Jing ; Zhang, Xue-Hui ; Cui, Ben-Cang ; Lin, Yuan-Hua ; Deng, Xu-Liang ; Li, Ming ; Nan, Ce-Wen
Assuntos: 3Y-TZP ; Aluminum Oxide - chemistry ; Bis-GMA ; Bisphenol A ; Bisphenol A-Glycidyl Methacrylate - chemistry ; Ceramics ; Ceramics - chemistry ; Composite materials ; Crack bridging ; Dental materials ; Dental Materials - chemistry ; Dental Porcelain - chemistry ; Dentin ; Dentistry ; Elastic Modulus ; Enamel ; Fracture toughness ; Hardness ; Hot Temperature ; Materials Testing ; Mechanical Phenomena ; Mechanical properties ; Microstructure ; Modulus of rupture in bending ; Nanocomposites ; Networks ; Pliability ; Polymers ; Polymers - chemistry ; Porosity ; Stress, Mechanical ; Teeth ; Tensile Strength ; Weibull distribution ; Zirconium - chemistry ; Zirconium dioxide
É parte de: Journal of dentistry, 2017-03, Vol.58, p.60-66
Notas: ObjectType-Article-1
SourceType-Scholarly Journals-1
ObjectType-Feature-2
content type line 23
Descrição: Abstract Objective The aim of this study was to evaluate the microstructure and mechanical behavior of polymer-infiltrated zirconia ceramics as a function of pre-sintering temperature (1000–1150 °C). Methods Polymer-infiltrated zirconia ceramics were prepared by combining the porous zirconia networks and polymer through infiltration and polymerization. XRD was employed to determine phase structure. The microstructure and fracture mechanism were observed by SEM. Flexural strength and fracture toughness were measured by three-point bending method and single-edge-notched beam method, respectively. A nanoindentation system was employed to determine elastic modulus and hardness. Results Different porosities and polymer contents can be obtained by tuning the pre-sintered temperature of zirconia ceramic precursors. Zirconia network porosity varies from 46.3% to 34.7% and the relevant polymer content ranges from 18.4 wt.% to 12.3 wt.% when the pre-sintered temperature is set from 1000 °C to 1150 °C. The flexural strength, fracture toughness, hardness, and elastic modulus values of the specimen pre-sintered at 1150 °C are 240.9 MPa, 3.69 MPa m1/2 , 3.1 GPa, and 58.8 GPa, respectively. Conclusion The pre-sintering temperature has a significant effect on the microstructure and mechanical properties of polymer-infiltrated zirconia ceramics and the optimal pre-sintering temperature is 1150 °C. Clinical significance Specimen pre-sintered at 1150 °C shows tooth-like mechanical properties, suggesting a promising restorative material in dental clinic. Moreover, the synthesis process is simple and can be easily performed in a prosthesis laboratory.
Editor: England: Elsevier Ltd
Idioma: Inglês;Persa

Links

View this record in MEDLINE/PubMed

Voltar para lista de resultados

Realização: Logos de Redes Sociais:

Mechanical performance of polymer-infiltrated zirconia ceramics

Li, Jing ; Zhang, Xue-Hui ; Cui, Ben-Cang ; Lin, Yuan-Hua ; Deng, Xu-Liang ; Li, Ming ; Nan, Ce-Wen

England: Elsevier Ltd

Buscando em bases de dados remotas. Favor aguardar.