Influence of friction surfacing process parameters to deposit AA6351-T6 over AA5052-H32 using conventional milling machine

Galvis, J.C. ; Oliveira, P.H.F. ; Hupalo, M.F. ; Martins, J.P. ; Carvalho, A.L.M.

Journal of materials processing technology, 2017-07, Vol.245, p.91-105 [Periódico revisado por pares]

Amsterdam: Elsevier B.V

Texto completo disponível

Citações Citado por
  • Título:
    Influence of friction surfacing process parameters to deposit AA6351-T6 over AA5052-H32 using conventional milling machine
  • Autor: Galvis, J.C. ; Oliveira, P.H.F. ; Hupalo, M.F. ; Martins, J.P. ; Carvalho, A.L.M.
  • Assuntos: AA5052-H32 aluminum alloy ; AA6351-T6 aluminum alloy ; Adhesive strength ; Bend tests ; Bending ; Conventional milling machine ; Deposition ; Feed rate ; Friction ; Friction surfacing ; Microhardness ; Microstructure ; Milling (machining) ; Process parameters ; Rolling direction ; Surfacing
  • É parte de: Journal of materials processing technology, 2017-07, Vol.245, p.91-105
  • Descrição: Superficial and microstructural characterization of the deposits was investigated. The substrate/deposit interface resistance was also investigated by bending tests and evaluating the microhardness profile. Consumable rods were deposited perpendicular to the plate rolling direction (DL); the rod rotation during the friction surfacing process was always clockwise and at room temperature. The control parameter deposition process was by the rod feed rate. Microscopic analysis has revealed the microstructural gradient transformation of the consumable rod during the friction surfacing process. Microhardness profile obtained along the rod has highlighted the presence of three distinct forming regions on the consumable material. Friction surfacing produced microstructural deposits of refined grains with 24.1% lower hardness values than those of the consumable material as received. The bending tests revealed delamination presence in the deposit/substrate interface with lower predominance for the 1A deposition process. The combination of the travel speed of 4mm/s and the increased rod feed rate (>5.7mm/s) can increase the adhesive strength of the deposit/substrate interface.
  • Editor: Amsterdam: Elsevier B.V
  • Idioma: Inglês
Voltar para lista de resultados
Ir para página anteriorAnterior Resultado  15 AvançarIr para próxima página

  • Realização: ABCD-USP USP   Logos de Redes Sociais: Freepik

Buscando em bases de dados remotas. Favor aguardar.