Parameter Optimization for the Electrospinning of La1-xSrxCo1-yFeyO3-[delta] Fibers for IT-SOFC Electrodes

Enrico, A ; Aliakbarian, B ; Lagazzo, A ; Donazzi, A ; Botter, R ; Perego, P ; Costamagna, P

Fuel cells (Weinheim an der Bergstrasse, Germany), 2017-08, Vol.17 (4), p.415 [Periódico revisado por pares]

Weinheim: Wiley Subscription Services, Inc

Texto completo disponível

Citações Citado por
  • Título:
    Parameter Optimization for the Electrospinning of La1-xSrxCo1-yFeyO3-[delta] Fibers for IT-SOFC Electrodes
  • Autor: Enrico, A ; Aliakbarian, B ; Lagazzo, A ; Donazzi, A ; Botter, R ; Perego, P ; Costamagna, P
  • Assuntos: Binder removal ; Electric potential ; Electrodes ; Electrospinning ; Evaporation ; Feeding ; Fibers ; Heating rate ; Nanofibers ; Perovskite structure ; Porosity ; Roasting ; Solid oxide fuel cells ; Thermogravimetric analysis
  • É parte de: Fuel cells (Weinheim an der Bergstrasse, Germany), 2017-08, Vol.17 (4), p.415
  • Descrição: La1-xSrxCo1-yFeyO3-[delta] (LSCF) fibers are synthesized through the single-needle electrospinning method. The formation of nanofibers is a function of the operating parameters, i.e., rotational speed of the support, solution feeding rate, and operating voltage, which are investigated experimentally in this work. The results show that a rotational speed of 750 rpm, a solution feeding rate of 0.5 mL h-1, and an operating voltage of 17 kV allow to obtain tissues with an average fiber diameter of 0.590 µm and porosity around 50%. The subsequent calcination processes are investigated through thermogravimetric analysis (TGA), which shows exothermic peaks due to solvent evaporation, debinding and perovskite structure formation, and suggest to perform calcination slowly in the temperature range 520-820 K. A fiber calcination process is carried out with a heating rate of 0.3 K min-1. Calcined fibers appear unbroken and visibly shrunk (post-calcination average diameter 0.31 µm), with a porosity of the calcined tissue of 51%. The morphological chacteristics of the LSCF calcined tissues are very promising for application in intermediate temperature solid oxide fuel cell (IT-SOFC) electrodes.
  • Editor: Weinheim: Wiley Subscription Services, Inc
  • Idioma: Inglês
Voltar para lista de resultados

  • Realização: ABCD-USP USP   Logos de Redes Sociais: Freepik

Buscando em bases de dados remotas. Favor aguardar.