Surface modification of EBF3-Fabricated Ti–6Al–4V parts by ultrasonic impact treatment

Panin, Alexey ; Kazachenok, Marina ; Perevalova, Olga ; Kolmakov, Alexey Panin, Victor E ; Fomin, Vasily M

AIP Conference Proceedings, 2020, Vol.2310 (1) [Periódico revisado por pares]

Melville: American Institute of Physics

Sem texto completo

Citações Citado por
  • Título:
    Surface modification of EBF3-Fabricated Ti–6Al–4V parts by ultrasonic impact treatment
  • Autor: Panin, Alexey ; Kazachenok, Marina ; Perevalova, Olga ; Kolmakov, Alexey
  • Panin, Victor E ; Fomin, Vasily M
  • Assuntos: Electron beams ; Freeform fabrication ; Grains ; Microstructure ; Post-processing ; Residual stress ; Surface finish ; Surface layers ; Three dimensional printing ; Titanium alloys ; Titanium base alloys
  • É parte de: AIP Conference Proceedings, 2020, Vol.2310 (1)
  • Descrição: Mechanical post-processing of 3D-printed components are required due to their poor surface finish, non-uniform microstructure and high residual stresses. Ultrasonic impact treatment can be successfully used for surface modification of Ti–6Al–4V titanium alloy parts manufactured by electron beam free-form fabrication. The gradient microstructure of the surface layers, produced in 3D-printed Ti–6Al–4V parts under ultrasonic impact treatment, was revealed using transmission electron microscopy. Non-equiaxial nanosized α-Ti grains were revealed in the outmost surface layer of 5–10 µm thick. α-Ti crystal grains with average size 150 nm are observed at depth of 20 µm beneath the specimen's surface. Finally, the average size of α-phase grains at a depth of 35 μm below the surface is equal to 400 nm. Orthorhombic α″ martensitic phase within fine α-Ti grains is observed. The mechanism of α″ phase formation during ultrasonic impact treatment is discussed.
  • Editor: Melville: American Institute of Physics
  • Idioma: Inglês
Voltar para lista de resultados
Ir para página anteriorAnterior Resultado  3 AvançarIr para próxima página

  • Realização: ABCD-USP USP   Logos de Redes Sociais: Freepik

Buscando em bases de dados remotas. Favor aguardar.