Tribological characterization of polyvinyl alcohol hydrogel as substitute of articular cartilage

Sardinha, V.M. ; Lima, L.L. ; Belangero, W.D. ; Zavaglia, C.A ; Bavaresco, V.P. ; Gomes, J.R.

Wear, 2013-04, Vol.301 (1-2), p.218-225 [Periódico revisado por pares]

Amsterdam: Elsevier B.V

Texto completo disponível

Citações Citado por
  • Título:
    Tribological characterization of polyvinyl alcohol hydrogel as substitute of articular cartilage
  • Autor: Sardinha, V.M. ; Lima, L.L. ; Belangero, W.D. ; Zavaglia, C.A ; Bavaresco, V.P. ; Gomes, J.R.
  • Assuntos: Articular ; Articular cartilage ; Biological and medical sciences ; Biotribology ; Cartilage ; Diseases of the osteoarticular system. Orthopedic treatment ; Friction ; Hydrogel ; Hydrogels ; Medical sciences ; Polyvinyl alcohol ; Polyvinyl alcohols ; Radiotherapy. Instrumental treatment. Physiotherapy. Reeducation. Rehabilitation, orthophony, crenotherapy. Diet therapy and various other treatments (general aspects) ; Surgical implants ; Tribology ; Wear
  • É parte de: Wear, 2013-04, Vol.301 (1-2), p.218-225
  • Notas: ObjectType-Article-1
    SourceType-Scholarly Journals-1
    ObjectType-Feature-2
    content type line 23
    ObjectType-Article-2
    ObjectType-Feature-1
  • Descrição: Polyvinyl alcohol (PVA) hydrogels are considered as promising biomaterials to substitute damaged articular cartilage due to their excellent biocompatibility, high permeability to fluids and low friction coefficient against smooth and wet surfaces. The study aims to demonstrate that under tribological loading mimicking in vivo conditions, PVA hydrogel/natural articular cartilage consists in a particular combination of mating surfaces with friction and wear characteristics compatible with the application as articular joints. Hydrogel membranes having approximately 1mm thickness were processed from PVA aqueous solutions (Aldrich Mw 89000–98000g/mol, 99% hydrolized), with 10% (w/w) concentration of polymer in solution, to be used as tribological samples against bovine articular cartilage. In order to ensure the natural properties and resistance of the tissue, articular cartilage samples were collected from condyles and prepared with ∼4mm subchondral bone. Tribological tests were performed on a pin-on-plate tribometer with a linear reciprocating geometry in the presence of distilled water and phosphate buffered saline solution (PBS) at 37°C. The reciprocating sliding frequency and stroke length were kept constant at 1Hz and 8mm, respectively. Contact pressures ranging from 1MPa to 5MPa were applied. For each experiment the friction coefficient was determined and the dominant wear mechanisms analyzed by SEM. The topography of hydrogel membranes in the hydrated state was evaluated with AFM microscopy for quantitative and qualitative analysis of worn surfaces. Results show that PVA hydrogel present excellent tribological performance against natural articular cartilage with very low friction coefficient values (≈0.02 to 0.05) combined with the preservation of both mating surfaces.
  • Editor: Amsterdam: Elsevier B.V
  • Idioma: Inglês